Ultra Broadband・Broadband Dieletric Half Mirror / PMH_PSMH
We offer Half-Mirror optics designed for use in Ultraviolet, Visible and Infrared wavelengths. They can be used for both transmission and divergence of multi-wavelength lasers and white light sources.
Ultra broadband half-mirrors are used for spectrometry applications.
Common Specifications
Material | BK7 Synthetic fused silica | |
---|---|---|
Surface Flatness | λ/10 | |
Coating | Front surface; Dielectric multilayer coating Rear surfaces; Anti-reflection coating |
|
Surface Flatness | 45° | |
Surface Quality (Scratch-Dig) | 10 - 5 | |
Clear Aperture | 90% of the diameter |
Schematic | Outline Drawing |
---|---|
Ultra broadband | |||||||
---|---|---|---|---|---|---|---|
Part Number | Wavelength Range | Diameter φD |
Thickness t |
Material | Parallelism | Transmittance (Average P and S) |
Laser Damage Threshold* |
PMH-25.4C03-10-25/7 | 250 - 700nm | φ25.4mm | 3mm | Synthetic fused silica | <5″ | 50±10%(average with respect to wavelength) | 0.5J/cm2 |
PMH-30C03-10-25/7 | 250 - 700nm | φ30mm | 3mm | Synthetic fused silica | <5″ | 50±10%(average with respect to wavelength) | 0.5J/cm2 |
PMH-50C05-10-25/7 | 250 - 700nm | φ50mm | 5mm | Synthetic fused silica | <5″ | 50±10%(average with respect to wavelength) | 0.5J/cm2 |
PMH-25.4C03-10-3/10 | 300 - 1000nm | φ25.4mm | 3mm | Synthetic fused silica | <5″ | 50±10%(average with respect to wavelength) | 0.5J/cm2 |
PMH-30C03-10-3/10 | 300 - 1000nm | φ30mm | 3mm | Synthetic fused silica | <5″ | 50±10%(average with respect to wavelength) | 0.5J/cm2 |
PMH-50C05-10-3/10 | 300 - 1000nm | φ50mm | 5mm | Synthetic fused silica | <5″ | 50±10%(average with respect to wavelength) | 0.5J/cm2 |
PMH-25.4C03-10-6/18 | 600 - 1800nm | φ25.4mm | 3mm | BK7 | <5″ | 50±10%(average with respect to wavelength) | 0.5J/cm2 |
PMH-30C03-10-6/18 | 600 - 1800nm | φ30mm | 3mm | BK7 | <5″ | 50±10%(average with respect to wavelength) | 0.5J/cm2 |
PMH-50C05-10-6/18 | 600 - 1800nm | φ50mm | 5mm | BK7 | <5″ | 50±10%(average with respect to wavelength) | 0.5J/cm2 |
PMH-25.4C03-10-4/20 | 400 - 2000nm | φ25.4mm | 3mm | BK7 | <5″ | 50±10%(average with respect to wavelength) | 0.5J/cm2 |
PMH-30C03-10-4/20 | 400 - 2000nm | φ30mm | 3mm | BK7 | <5″ | 50±10%(average with respect to wavelength) | 0.5J/cm2 |
PMH-50C05-10-4/20 | 400 - 2000nm | φ50mm | 5mm | BK7 | <5″ | 50±10%(average with respect to wavelength) | 0.5J/cm2 |
*Laser pulse width 10ns, repetition frequency 20Hz
Broadband | |||||||
---|---|---|---|---|---|---|---|
Part Number | Wavelength Range | Diameter φD |
Thickness t |
Material | Parallelism | Transmittance (Average P and S) |
Laser Damage Threshold* |
PSMH-25.4C03-10-550 | 400 - 700nm | φ25.4mm | 3mm | BK7 | <5″ | 50±5%(average with respect to wavelength) | 2.1J/cm2 |
PSMH-30C03-10-550 | 400 - 700nm | φ30mm | 3mm | BK7 | <5″ | 50±5%(average with respect to wavelength) | 2.1J/cm2 |
PSMH-30C05-10W-550 | 400 - 700nm | φ30mm | 5mm | BK7 | 1°±5′ | 50±5%(average with respect to wavelength) | 2.1J/cm2 |
PSMH-40C04-10-550 | 400 - 700nm | φ40mm | 4mm | BK7 | <5″ | 50±5%(average with respect to wavelength) | 2.1J/cm2 |
PSMH-50C05-10-550 | 400 - 700nm | φ50mm | 5mm | BK7 | <5″ | 50±5%(average with respect to wavelength) | 2.1J/cm2 |
PSMH-50C08-10W-550 | 400 - 700nm | φ50mm | 8mm | BK7 | 1°±5′ | 50±5%(average with respect to wavelength) | 2.1J/cm2 |
PSMH-30C03-10-800 | 700 - 900nm | φ30mm | 3mm | BK7 | <5″ | 50±3%(800nm) | 2.1J/cm2 |
PSMH-30C05-10W-800 | 700 - 900nm | φ30mm | 5mm | BK7 | 1°±5′ | 50±3%(800nm) | 2.1J/cm2 |
PSMH-50C05-10-800 | 700 - 900nm | φ50mm | 5mm | BK7 | <5″ | 50±3%(800nm) | 2.1J/cm2 |
PSMH-50C08-10W-800 | 700 - 900nm | φ50mm | 8mm | BK7 | 1°±5′ | 50±3%(800nm) | 2.1J/cm2 |
PSMH-30C03-10-1400 | 1350 - 1550nm | φ30mm | 3mm | BK7 | <5″ | 50±3%(1400nm) | 2.1J/cm2 |
PSMH-30C05-10W-1400 | 1300 - 1550nm | φ50mm | 5mm | BK7 | 1°±5′ | 50±3%(1400nm) | 2.1J/cm2 |
*Laser pulse width 10ns, repetition frequency 20Hz